VE-TP is an ultra-high transparent EVA film developed by E&N for ultra-clear glass lamination. Its laminated glass has the characteristics of ultra-high permeability and impact resistance.The scope of application is ultra-clear glass laminated and wired glass. Jewelry cabinets, display case laminated glass and other laminated wire glass with strict requirements on transparency.
HJ25TP:
|
|
HJ38TP:
|
|
HJ50TP:
|
|
HJ76TP:
|
|
HJ-TP:
|
|
Main Characteristic:
1.Ultra-high transparency,ultra-high whiteness,effectively improve the visual transparency of ultra-white laminated glass
2.Ultra-low haze,can also show the transparency of ultra-white glass under strong light concentrated irradiation
3.Weather resistance,adhesion and impact resistance all meet the requirements of outdoor building grades
Application:
1.Ultra-clear glass lamination
2.Jewelry cabinet, display cabinet laminated glass
3.Other laminated glass with strict requirements on transparency
Product Performance Parameter List:
Test item |
Test method |
HJ-TP |
Transmittance |
ISO527-3 |
>91% |
Haze |
E&N Laboratory |
<0.15% |
UV blocked rate |
280-380nm |
/ |
Tensile strength |
ISO527-3 |
>17MPa |
Adhesion with glass |
ISO-8510 |
>95N/cm |
Elongation at break |
ISO527-3 |
≥800% |
Cross-linking rate |
E&N Laboratory |
>85% |
Water absorption |
ASTMAD570 |
≤0.1% |
High temperature test 4hrs 100℃ |
EN 14449/EN1SO12543 |
No visible change |
Humidity resistance 85℃ 85%RH 1000hrs |
ENISO12543 |
Haze appeared just 2.5cm from the edge without bubbles or delamination |
UV radiation test UVA340 60℃ 65%RH 2000hrs |
EN14449/EN572 |
Yellowing index:Δ<1 |
Pendulum test(hight:1200mm) |
EN14449/EN 12600 |
Qualified |
Ball impact peeling resistance(hight:4m) |
GB-15763.3-2009 |
Qualified |
Note:the information and relevant data listed in this article are established in the laboratory of the company's technical department,and their contents are correct based on the turth.However,we will not make any statement or guarantee on the integrity or accuracy of the listed information and data.We provide the content of this article on the condition that it is for the user's reference only,and before using it,decide whether the information and data are suitable for their own purpose of use.In no event shall we be liable or liable for damages of any nature whatsoever arising out of the use of or reliance on the content of this document or the products mentioned herein.
Packing Specification:
1.Without plywood case: tinfoil vacuum + bubble wrap + composite kraft paper
2.With plywood case: tinfoil vacuum + carton box + plywood case
Shelf Life of Product:
1 year
Preparation Before Laminating:
1. Clean and fully dry the glass, there should be no particle dust or oil on the glass surface, EVA film and other intermediate materials are spare.
2. After opening the furnace, cool down for 3~5 minutes, until the vacuum value reaches -0.095MPa, close the furnace door and officially heat.
Parameter setting:
First Step |
Second Step |
Full Vacuum Retention |
Temperature Out of Furnace |
60℃—20mins |
125℃—45mins |
-0.095MPa |
<50℃ |
The above-mentioned temperature refers to the glass surface temperature.This lamination parameter is suitable for laminated glass with 5mm+0.38EVA+5mm structure.The specific conditions should be adjusted according to the difference of lamination equipment,temperature and humidity,glass thickness,and middle layer material.
1.Can it be used outdoors?
Sure.
2.What is the difference between degree of crosslinking and UV blocking rate?
The degree of cross-linking affects whether the product can be applied outdoors. In general, products with a degree of cross-linking >85% can be applied outdoors. The UV blocking ratio only determines the blocking ratio of the product to UV rays, and has nothing to do with whether the product can be applied outdoors.
3.Why does HJ-TP have a longer lead time?
Because the order of HJ-TP is relatively small, and our production will be arranged according to the order.
4.Why is the actual thickness measured by the product a little thicker?
Because the product has embossing, some places have deep embossing, and some places have shallow embossing, the measured thickness will be different.
5.Does HJ-TP have fragment retention capabilities?
Yes, this is the basic performance of all our products.